Aluminum Oxide Grit size 220

Aluminum Oxide Grit size 220

/MT

Aluminum Oxide Grit size 220

Brown fused alumina is produced by the smelting of Calcined Bauxite in an electric arc furnace at temperatures greater than 2000°C. Our BFA is made into different shapes and grit sizes ranging from macro to micro grits and powders. It is a tough, hard material with high strength, excellent wear and corrosion resistance and good thermal conductivity.

Brown fused aluminum oxide are available in standard grit and powder sizes and they can also be made to individual specifications. Please see below for information about some of our fused aluminum oxide materials.

ApplicationTypeSizeChemical composition(%)
Al2O3Fe2O3SiO2TiO2
refractorySand0-1mm95 Min0.3 Max1.5 Max3.0 Max
1-3mm
3-5mm
5-8mm
Fine powder100mesh94.5 Min0.5 Max1.5 Max3.0 Max
200 mesh
325 mesh
Hardness9.0 mohs
Working Temp1900℃
Melting Point2200℃
ApplicationSizeChemical composition(%)
Al2O3Fe2O3SiO2TiO2
Abrasives12#-54#≥95≤0.5≤1.5≤3.0
54#-120#≥94
150#-240#≥93
240#-400#≥94≤2.0≤1.5≤3.0
600#-1000#≥93.5
1000#-1500#≥93≤2.0≤1.5≤3.0

♦Application(Aluminum Oxide Grit size 220)

1.Abrasive: Produce ceramic grind wheel, resinoid grinding wheel, Grinding stone, Grinding block, sand paper, sand cloth, sand belt, polish wax, abrasive paste, coating etc..
2.Refractory material: Mainly used for abrasion and high temperature resistant, inoxidizable aggregate and filling of shaped and monolithic refractory in steel metallurgy, various industrial stoves, electric furnace etc..
3.Sandblasting abrasive: Mainly used for various material workpieces to decontaminate, derusting, prevent corrosion, remove oxide skin etc..
4.Abrasion resistance ground: Mainly used for non-slip of airport and road, chemical factory board paving.
5.Precision casting: Investment casting technics of stainless steel and aluminium casting in coating.